陶瓷盘专用版特性:
【1】特殊调制无金属配方设计，利于碳陶盘，也适用于普通刹车盘，各种场景都可应用，不推荐跑赛道长时间制动。
【2】碳纤维高碳陶瓷皮，添加芳纶纤维、进口石墨进口焦炭、耐高温强度更大，低温高温摩擦系数比较平稳，配方
专为陶瓷盘设计，不含钢棉，高温后不伤盘，粉尘极少，静音表现良好，耐磨。对场景无特殊要求，注意温度区间，
出于安全考虑，建议留足散热时间，不推荐跑赛道长时间制动。
【3】瞬时盘面接触温度可耐800℃，长时使用控制在盘温不超550℃为宜，设计摩擦系数0.445。*
* 温度值为实验室数据，普通盘使用时建议盘面颜色控制在蓝紫色状态内为宜。长时间高温使用，制动性能会有下降风险。
* 摩擦系数标示为换算至GB5763-2008版标准对应值，按照新国际GB5763-2018标准为PS0.380+-15%。
【1】Designed with a specially formulated metal-free composition, it is suitable for carbon-ceramic discs and also works with ordinary brake discs. It can be used in various scenarios, but prolonged braking on race tracks is not recommended.
【2】It adopts carbon fiber high-carbon ceramic pads, with added aramid fibers, imported graphite, and imported coke, providing higher high-temperature resistance strength. The friction coefficient remains relatively stable at both low and high temperatures. The formula is specifically designed for ceramic discs, containing no steel wool, so it will not damage the discs after exposure to high temperatures. It produces extremely low dust, offers good quiet performance, and has high wear resistance. There are no special requirements for application scenarios, but attention should be paid to the temperature range. For safety reasons, it is recommended to allow sufficient cooling time, and prolonged braking on race tracks is not recommended.
【3】The instantaneous disc contact temperature can withstand up to 800℃, and it is advisable to control the disc temperature below 550℃ during prolonged use. The designed friction coefficient is 0.445.*
*The temperature values are laboratory data. When used with ordinary discs, it is recommended to keep the disc color within the blue-purple range. Prolonged use at high temperatures may pose a risk of reduced braking performance.
*The indicated friction coefficient is the corresponding value converted according to the GB5763-2008 standard, and it is PS0.380±15% in accordance with the new national standard GB5763-2018.